Preparation and performance of bisimidazole cationic crosslinked addition-type polynorbornene-based anion exchange membrane

The late transition metal catalyst system (η³-allyl)Pd(PPh₃)Cl/Li[B(C₆F₅)₄]·2.5Et₂O (Li[FABA]) was used to catalyze 5-norbornene-2-methylenehexyl ether (NB-MHE) and 5-norbornene-2-methylene-(6-bromohexyl) ether (NB–O–Br) controllable addition copolymerization to obtain post-functionalized vinyl addition-type block copolymer aP(NB-O-Br-b-NB-MHE). 1,6-Bis(2-methylimidazole)hexane (Bis-MeIm) was used as a crosslinking agent to prepare a series of anion exchange membranes (AEMs) CL-aP(NB-O-Br-b-NB-MHE). The initial thermal decomposition temperature of the obtained addition-type polynorbornene-based AEM was about 250 °C. The AEM had moderate water uptake (WU) and swelling ratio (SR), and obvious micro-phase separation structure that could be observed from the AFM phase diagram. It could maintain high OH^? conductivity (85.07 mS cm^?1, 80 °C) and alkali resistance stability (soaking alkali for more than 500 h at 25 °C). In the single cell test of the H₂/O₂ fuel cell assembled by CL5-aP(NB-O-Br-b-NB-MHE), the peak power density was 177 mW cm^?2.