Mechanistic studies in tackified acrylic emulsion pressure sensitive adhesives

Twenty‐three wt % aqueous tackifier dispersion based on glycerol ester abietic acid (T_g = 64°C, M_w = 940) was added to emulsion polymer 50/32/15/3 poly(2‐ethyl hexyl acrylate‐co‐vinyl acetate‐co‐dioctyl maleate‐co‐acrylic acid) pressure sensitive adhesive (PSA). From these latices, 25 μm thick films were cast. The films were dried at 25°C for 24 h or at 121°C for 5 min. Dynamic mechanical analysis (DMA) of the films included measuring elastic modulus (G′) and damping factor (tan δ). Under the above drying conditions, the films did not produce significant differences in their DMA and PSA properties as measured by loop tack, peel, and shear holding power. DMA of the tackified acrylic film showed thermodynamic miscibility between the tackifier and polymer regardless of the drying conditions. Microgels formed during emulsion polymerization of the acrylic PSA brought inherent weakness to the tackified film properties. In the neat acrylic PSA film, these discrete networks entangled with the uncrosslinked chains while in the tackified film, these networks could not form entanglements due to the increased molecular weight between entanglements for the uncrosslinked chains. This lack of network entanglements caused shear holding power of the tackified acrylic PSA film to be 4× lower than that of the neat acrylic PSA film. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 76: 1965–1976, 2000