Enhanced electrochemical performance and thermal stability of La2O3-coated LiCoO2

An enhanced electrochemical performance LiCoO₂ cathode was synthesized by coating with various wt.% of La₂O₃ to the LiCoO₂ particle surfaces by a polymeric method, followed by calcination at 923 K for 4 h in air. The surface-coated materials were characterized by XRD, TGA, SEM, TEM, BET and XPS/ESCA techniques. XRD patterns of La₂O₃-coated LiCoO₂ revealed that the coating did not affect the crystal structure, α-NaFeO₂, of the cathode material compared to pristine LiCoO₂. TEM images showed a compact coating layer on the surface of the core material that had an average thickness of about ∼15 nm. XPS data illustrated that the presence of two different environmental O 1s ions corresponds to the surface-coated La₂O₃ and core material. The electrochemical performance of the coated materials by galvanostatic cycling studies suggest that 2.0 wt.% coated La₂O₃ on LiCoO₂ improved cycle stability (284 cycles) by a factor of ∼7 times over the pristine LiCoO₂ cathode material and also demonstrated excellent cell cycle stability when charged at high voltages (4.4, 4.5 and 4.6 V). Impedance spectroscopy demonstrated that the enhanced performance of the coated materials is attributed to slower impedance growth during the charge-discharge processes. The DSC curve revealed that the exothermic peak corresponding to the release of oxygen at ∼464 K was significantly smaller for the La₂O₃-coated cathode material and recognized its high thermal stability.