交联聚酰亚胺的减摩增韧改性 |
| |
引用本文: | 丛培红 李家泽. 交联聚酰亚胺的减摩增韧改性[J]. 工程塑料应用, 1997, 25(2): 1-4 |
| |
作者姓名: | 丛培红 李家泽 |
| |
作者单位: | 中国科学院兰州化学物理研究所 730000(丛培红,李同生,张绪寿),中国科学院化学研究所 北京(李家泽) |
| |
摘 要: | 采用短碳纤维(CF)、聚四氟乙烯(PTFE)和缩合型线性聚酰亚胺(CPI),用机械共混、热压模塑的方法,对加成型交联聚酰亚胺(API)进行减摩增韧性性,并对复合材料的摩擦磨损、力学性能和形态结构进行了测试与分析。研究结果表明,与纯API相比,含10%CF的API复合材料的冲击强度提高了280%;含20%CPI的API复合材料的冲击强度,弯曲强度分别提高了150%和60%;含30TPTEE的API复
|
关 键 词: | 聚酰亚胺 碳纤维 复合材料 增韧 摩擦 改性 |
PHYSICAL MODIFICATION OF CROSS-LINKING POLYIMIDE |
| |
Abstract: | Tribological and mechanical properties of short carbon fiber (CF),polytetrafluoroethyIene ( PTFE ),condensation-type linear polyimide (CPI) filled addition-type cross-linking polyimide (API) were studied in this paper.Structural morphology were analyzed by means of Scanning Electron Microscope (SEM).It was found that,the content of CF was 10%.impact strength of composite was 280% times of API.Friction coefficient of 30% PTFE filled API reduced to 0.16,wear decreased to 0.3 urn3.The content of CPI was 20%,impact strength and flexural strength of composite were 250%,160% times of API respectively.Fillers which were compatible with API,could improve toughness and flexural strength of composites simultaneously. |
| |
Keywords: | polyimide carbon fiber PTFE composite tougheness friction |