Low-Temperature High-Pressure Consolidation of Amorphous Al2O3–15 mol% Y2O3

This study examined pressure consolidation of amorphous Al₂O₃–15 mol% Y₂O₃ powders prepared by co-precipitation and spray pyrolysis. The two amorphous powders had similar true densities and crystallization sequences. Uniaxial hot pressing was carried out at 450°–600°C with a moderate pressure of 750 MPa. The co-precipitated powder could be hot pressed to a maximum relative density of 98% and remained amorphous. Pressure adversely affected the densification of the spray-pyrolyzed powder by favoring an early crystallization of γ-Al₂O₃ phase at 580°C. Plastic deformation of the amorphous phase is believed to be responsible for the large densification of the amorphous powders.