Improvement of the Magnetization of Barium Hexaferrites Induced by Substitution of Nd3+ Ions for Fe3+ Ions

Barium hexagonal ferrites (BaNd _x Fe_12?x O ₁₉) have been synthesized by initial high-energy milling of the precursors and calcining subsequently. The as-prepared samples are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometry (VSM). XRD and SEM examinations reveal that a high-crystallized hexagonal BaNd _x Fe_12?x O ₁₉ with lamellar morphology is obtained when the precursor is calcined at 1200^°C in air for 3 h. The hexagonal crystalline structure of BaFe₁₂ O ₁₉ is not changed after doping Nd³⁺ ions in BaFe₁₂ O ₁₉. However, lattice parameters a and b values increase with an increase in Nd content at first, then decrease. Nd substitution may improve the magnetic properties of BaNd _x Fe_12?x O ₁₉. BaNd_0.1Fe_11.9 O ₁₉, obtained at 1050^°C, has the highest specific saturation magnetization value (80.81 emu/g) and magnetic moment (16.21 μ _B); BaNd_0.2Fe_11.8 O ₁₉, obtained at 950^°C, has the highest coercivity value, 4075.19 Oe.