| 热处理对La_(0.53)Ce_(0.47)Ni_(3.4)Co_(0.6)Mn_(0.3)Cu_(0.1)合金相结构和储氢性能的影响 |
| |
| 引用本文： | 曹慧,柳召刚,徐津,王剑辉,罗淇文,吉力强. 热处理对La_(0.53)Ce_(0.47)Ni_(3.4)Co_(0.6)Mn_(0.3)Cu_(0.1)合金相结构和储氢性能的影响[J]. 有色金属(冶炼部分), 2016, 0(6): 58-61 |
| |
| 作者姓名： | 曹慧 柳召刚 徐津 王剑辉 罗淇文 吉力强 |
| |
| 作者单位： | 内蒙古科技大学 材料与冶金学院,内蒙古科技大学 材料与冶金学院,内蒙古稀奥科贮氢合金有限公司,内蒙古科技大学 材料与冶金学院,内蒙古包头稀土研究院;内蒙古包头稀土研究院,内蒙古稀奥科贮氢合金有限公司 |
| |
| 基金项目： | 国家自然科学基金资助项目（51564040）；国家火炬计划项目（2014GH710301）；内蒙古自然科学基金项目（2015MS0218） |
| |
| 摘 要： | 采用感应熔炼法制备La_(0.53)Ce_(0.47)Ni_(3.4)Co_(0.6)Mn_(0.3)Cu_(0.1)储氢合金,并在不同温度下进行热处理,通过XRD对其相组成及结构进行表征,并采用双电极模拟电池测试系统对其储氢性能进行测试与分析。结果表明,随着退火温度的升高,合金的相组成未发生变化,但其晶化程度逐渐增高,晶体缺陷和晶格应力逐渐减少。热处理改善了合金的循环稳定性,提高了合金的电化学容量,但恶化了高倍率放电能力。
|
| 关 键 词： | 热处理 储氢合金 相结构 电化学性能 |
| 收稿时间： | 2015-12-16 |
| 修稿时间： | 2015-12-28 |
Effect of Heat Treatment on Structure and Hydrogen Storage Property of La0.53Ce0.47Ni3.4Co0.6Mn0.3Cu0.1 Alloy |
| |
| caohui,Liu Zhaogang,Xu Jin,Wang Jianhui,Luo Qiwen and Ji Liqiang. Effect of Heat Treatment on Structure and Hydrogen Storage Property of La0.53Ce0.47Ni3.4Co0.6Mn0.3Cu0.1 Alloy[J]. Nonferrous Metals(Extractive Metallurgy), 2016, 0(6): 58-61 |
| |
| Authors: | caohui Liu Zhaogang Xu Jin Wang Jianhui Luo Qiwen Ji Liqiang |
| |
| Affiliation: | Inner Mongolia Rare Earth Ovonic Metal Hydride Co.Ltd,,,,, |
| |
| Abstract: | La0.53Ce0.47Ni3.4Co0.6Mn0.3Cu0.1 alloy was prepared by induction melting and annealed under different temperatures. Phase composition and structure were characterized by XRD, hydrogen storage performance was tested and analyzed by two-electrode cell simulation test system. The results show that with increase of annealing temperature, composition of alloy presents no change, but crystallization degree and grain size increase gradually. Discharge capacity and cycle stability of alloy are improved by annealing treatment, but high-rate discharge capacity of alloy is deteriorated. |
| |
| Keywords: | heat treatment hydrogen storage alloy phase structure electrochemical properties |