C60抗冲磨混凝土抗裂性能试验研究

为提供性能优异的抗冲磨混凝土配制方案,以单掺或复掺粉煤灰、矿渣粉、硅粉配制的C60抗冲磨混凝土为研究对象,通过平板法和圆环法对C60抗冲磨混凝土的抗裂性能进行研究.研究结果表明:①保持水胶比不变的情况下,掺入粉煤灰或矿渣粉均可降低混凝土的体积收缩变形、延长混凝土开裂时间;②随着粉煤灰或矿渣粉掺量的增加,抑制混凝土开裂的...

Experimental Study on Anti-crack Performance of Wear Resistant Concrete C60

To offer superior mix proportion scheme for wear resistant concrete, we prepared C60 anti-wear concrete specimens by adding merely or mixed fly ash, slag powder and silica fume, and tested the crack resistance of the specimens using the plane method and the ring method. Research results demonstrate that: 1) when the water-to-binder ratio remains unchanged, the incorporation of fly ash or slag powder reduces the volumetric shrinkage deformation of concrete and prolongs the cracking time of concrete; 2) with the increase of fly ash or slag powder, the effect of restraining concrete cracking tends to be obvious; 3) the incorporation of silica fume evidently promotes the cracking of concrete, and such cracking gets more severe when the amount of silica fume increases, and the cracking of concrete tends to be serious; 4) the synergistic complementary effect formed by the fusion of silica fume and fly ash or slag powder reduces the cracking of C60 anti-wear concrete. The anti-cracking effect is optimal when 15% fly ash and 7% silica fume are compounded.