Analysis of various versions of the deoxidation of rail steel at OAO NTMK

The deoxidation of steel melted using various types of deoxidizers during out-of-furnace treatment is studied. The total oxygen and nitrogen content and the oxygen contents in the main types of oxide nonmetallic inclusions are determined by fractional gas analysis of steel samples taken from heats performed by various schedules. The main types of nonmetallic inclusions and their size distributions are found with qualitative and quantitative metallography. The oxygen content in the rail steel is minimal (5 ppm) when calcium carbide CaC₂ is introduced into the metal in tapping of a converter. When the metal is deoxidized using a steel wire filled with calcium or a steel wire filled with silicocalcium, the oxygen content in rail steel is ≈8 and ≈11 ppm, respectively. A comparison of various processes of rail steel deoxidation under the OAO NTMK conditions shows that the limitation of the aluminum content (no more than 30 ppm) or the use of a wire with a calcium or calcium carbide filler is more effective than the use of a wire filled with silicocalcium.