| 高温过热器T91管爆裂原因分析 |
| |
| 引用本文： | 曹品彪,班新华. 高温过热器T91管爆裂原因分析[J]. 贵州电力技术, 2014, 0(10): 32-34 |
| |
| 作者姓名： | 曹品彪 班新华 |
| |
| 作者单位： | 贵州电力试验研究院,贵州贵阳550002 |
| |
| 摘 要： | 通过宏观检查，光谱分析，壁厚分析以及金相组织分析方法，对某电厂300WM高温过热器T91管爆口附近管样进行分析，结果表明；由于钢管长期超温运行，过热使其爆口附近显微组织老化，晶界出现空洞和裂纹，力学性能显著下降，从而在厚度减薄区域发生爆裂。
|
| 关 键 词： | T91 过热器 爆管 超温 纵向裂纹 老化 |
Analysis on the explosion reason for high temperature over-heater T91 tube |
| |
| CAO Pingbiao,BAN Xinhua. Analysis on the explosion reason for high temperature over-heater T91 tube[J]. Guizhou Electric Power Technology, 2014, 0(10): 32-34 |
| |
| Authors: | CAO Pingbiao BAN Xinhua |
| |
| Affiliation: | (Guizhot, Eleclric Power Testing ＆ Research Institute, Guiyang 550002 Guizhou, China) |
| |
| Abstract: | Through macro inspection, spectral analysis, wall thickness analysis and metallographic structure analysis, the sample near the explosion of high temperature over-heater T91 was analyzed. The result showed that the long-term over temperature operation leaded to the aging of the micro organization near explosion, the hole and crack of grain boundary, and reduction of mechanical properties, so the explosion was happened near the area of thickness thinning. |
| |
| Keywords: | T91 over-heate, r explosion tube over temperature longitudinal crack aging |