| Abstract: | The effect of γ-irradiation on the performance of wet cellulose acetate membranes in the dose range of 2.5–10 Mrads was investigated using a 60Co source. Changes in transport properties and inherent viscosity of the membranes suggested continued degradation as a result of irradiation. Solubility and specific gravity changes accompanying irradiation indicated some sort of structural aggregation occuring at higher doses. Consumption of dissolved oxygen during irradiation and the extent of deacetylation of the membrane polymer were determined to study the kinetics of the degradative process. Analysis of the end products of irradiation was attempted by UV spectroscopy. ESR spectra of membrane polymer after irradiation were analyzed to identify the free radicals generated. A tentative mechanism of radiolytic degradation causing the observed performance failure is proposed. |