Effect of Atmosphere and Temperature on the Tribological Behavior of the Ti Containing MoS2 Coatings Against Aluminum

MoS₂ coatings exhibit low coefficient of friction (COF) when sliding against aluminum; however, the magnitudes of their COF show high sensitivity to environmental conditions. Ti could reduce the sensitivity of the frictional behavior of MoS₂ coatings to moisture. This study examines the tribological properties of Ti containing MoS₂ coating (Ti–MoS₂) tested against an aluminum alloy (Al-6.5% Si) in ambient air (58% relative humidity, RH), dry oxygen, dry air and dry N₂ (< 4% RH) atmospheres. The Ti–MoS₂ coating exhibited similar COF values under an ambient (0.14), dry oxygen (0.15) and dry air (0.16) atmospheres. It was found that oxidation of MoS₂ to MoO₃ was responsible for high COF under these testing conditions as revealed by Energy-dispersive X-ray Spectroscopy (EDS) and micro-Raman spectroscopy. However, a low and stable COF of 0.07 was observed under a dry N₂ condition. This work further showed that the tests performed at elevated temperatures, up to 400 °C in a dry N₂ atmosphere sustained the low and stable COF of the Ti–MoS₂ coatings. The sliding tests performed under a dry N₂ atmosphere prevented the formation of MoO₃ and as a result, the Ti–MoS₂ coatings maintained low COF values. Low COF values were also attributed to the formation of MoS₂ transfer layers.