Characterization of Pr1−xSrxCo0.8Fe0.2O3−δ (0.2 ≤ x ≤ 0.6) cathode materials for intermediate-temperature solid oxide fuel cells

Cathode materials consisting of Pr_1−xSr_xCo_0.8Fe_0.2O_3−δ (x = 0.2–0.6) were prepared by the sol–gel process for intermediate-temperature solid oxide fuel cells (IT-SOFCs). The samples had an orthorhombic perovskite structure. The electrical conductivities were all higher than 279 S cm⁻¹. The highest conductivity, 1040 S cm⁻¹, was found at 300 °C for the composition x = 0.4. Symmetrical cathodes made of Pr_0.6Sr_0.4Co_0.8Fe_0.2O_3−δ (PSCF)–Ce_0.85Gd_0.15O_1.925 (50:50 by weight) composite powders were screen-printed on GDC electrolyte pellets. The area specific resistance value for the PSCF–GDC cathode was as low as 0.046 Ω cm² at 800 °C. The maximum power densities of a cell using the PSCF–GDC cathode were 520 mW cm⁻², 435 mW cm⁻² and 303 mW cm⁻² at 800 °C, 750 °C and 700 °C, respectively.