Development of selectively densified surface laminated wood based composites

An attempt was made to develop selectively densified surface laminated wood based composites. Two types of wood composites were produced (veneer laminated Medium Density Fiberboard, MDF and wafer overlaid particleboard, PB) in this study. Veneer or wafer plasticized by NaClO₂ treatment and PF resin impregnated were laminated on both sides of the MDF or PB and compressed at ordinary pressure. The main observation was that overlaying plasticized veneer on MDF before hot pressing is a promising method for improving mechanical properties and dimensional stability of commercial MDF. The MOR and MOE of surface laminated MDF attained 177 MPa and 18 GPa, respectively. The water absorption percentage of laminated MDF decreased from 160.7 to 7.2%. Furthermore, it is interesting to note that NaClO₂ treated and resin impregnated wafer or powder laminated particleboards showed excellent performance especially in stiffness. The MOR and MOE reached 40 MPa and 7 GPa which is more than two times higher compared to untreated wafer laminated board and three times higher than particleboard. This value is comparable to commercial lauan plywood having a density of 0.78 g/cm³. The processing technique of the composite is simple and can be easily applied by the industry.