| 氟碳涂料中主组分对涂层性能的影响 |
| |
| 引用本文： | 郭小翠,周永言,李丽,王敏,熊书华,朱志平. 氟碳涂料中主组分对涂层性能的影响[J]. 材料保护, 2011, 44(11): 25-28,7 |
| |
| 作者姓名： | 郭小翠 周永言 李丽 王敏 熊书华 朱志平 |
| |
| 作者单位： | 1. 长沙理工大学化学与生物工程学院,湖南长沙,410114
2. 广东电网公司电力科学研究院,广东广州,510080 |
| |
| 基金项目： | 湖南省自然科学基金项目(09JJ6067);湖南省科技攻关项目(2010GK3171);湖南省研究生创新基金项目(CX2009B182、CX2010B364)资助 |
| |
| 摘 要： | 为促进低表面能氟碳涂料的研究应用，使用能谱仪（EDS）、扫描电镜（SEM）、接触角测量仪和划格试验法对FEVE（氟烯烃一乙烯基醚或酯的共聚物）氟碳涂料涂膜表面进行表征和测试，考察了氟碳涂料中的偶联剂、填料及颜料含量对涂层性能的影响。结果表明：涂层表层比底层的氟含量要高，且存在纳米级的“突起”；偶联剂含量大于3．O％时涂...
|
| 关 键 词： | FEVE氟碳涂料 偶联剂 金红石型Ti02 气相Si02 憎水性 附着力 耐腐蚀性能 |
Effect of Composition of Fluorocarbon Resin Paint on Performance of the Coatings |
| |
| GUO Xiao-cui,ZHOU Yong-yan,LI Li,WANG Min,XIONG Shu-hua,ZHU Zhi-ping. Effect of Composition of Fluorocarbon Resin Paint on Performance of the Coatings[J]. Journal of Materials Protection, 2011, 44(11): 25-28,7 |
| |
| Authors: | GUO Xiao-cui ZHOU Yong-yan LI Li WANG Min XIONG Shu-hua ZHU Zhi-ping |
| |
| Affiliation: | 1(1.School of Chemical and Biological Engineering,Changsha University of Science & Technology, Changsha 410114,China;2.Research Institute of Electric Power,Guangdong Power Grid Corporation,Guangzhou 510080,China). |
| |
| Abstract: | The effects of coupling agent,pigment and filler used in fluorocarbon resin paint on the performance of the coatings made of the fluorocarbon resin paint were investigated based on energy dispersive spectrometric analysis,scanning electron microscopic analysis, contact angle tests and scratching tests.Results show that the surface of the coatings has a higher fluorine content than the underlayer, and contains nano-sized protrusions.The coatings made of the paint with coupling agent content of above 3.0%possessed stronger hydrophobicity and adhesion to substrate,but their corrosion resistance remained almost unchanged.Increasing content of rutile TiO2 in the paint resulted in reduced hydrophobicity as well as increased adhesion and corrosion resistance of the coatings. Moreover,gas-phase SiO2 had little effect on the hydrophobicity of the coatings.With increasing content of SiO2,the adhesion of the coatings was reduced,and the corrosion resistance of the coatings initially rose but later declined therewith.The fluorocarbon coatings made of the paint consisting of 5.5%- 8.5% coupling agent,2.0% 6.0%TiO2 and 2.5 6.1%SiO2 possessed better performance. |
| |
| Keywords: | fluorocarbon paint coupling agent rutile TiO2 gasphase SiO2 hydrophobicity adhesion corrosion resistance |