The Microstructure Evolution of Dual-Phase Pipeline Steel with Plastic Deformation at Different Strain Rates |
| |
| Authors: | L K Ji T Xu J M Zhang H T Wang M X Tong R H Zhu G S Zhou |
| |
| Affiliation: | 1.Tubular Goods Research Institute of CNPC,Xi’an,China;2.State Key Laboratory of Performance and Structural Safety for Petroleum Tubular Goods and Equipment Materials,Xi’an,China;3.State Key Laboratory for Mechanical Behavior of Materials,Xi’an Jiaotong University,Xi’an,China;4.School of Materials Science and Engineering,Xi’an Jiaotong University,Xi’an,China;5.Pressure Pipeline Department,China Special Equipment Inspection and Research Institute,Beijing,China |
| |
| Abstract: | Tensile properties of the high-deformability dual-phase ferrite-bainite X70 pipeline steel have been investigated at room temperature under the strain rates of 2.5 × 10?5, 1.25 × 10?4, 2.5 × 10?3, and 1.25 × 10?2 s?1. The microstructures at different amount of plastic deformation were examined by using scanning and transmission electron microscopy. Generally, the ductility of typical body-centered cubic steels is reduced when its stain rate increases. However, we observed a different ductility dependence on strain rates in the dual-phase X70 pipeline steel. The uniform elongation (UEL%) and elongation to fracture (EL%) at the strain rate of 2.5 × 10?3 s?1 increase about 54 and 74%, respectively, compared to those at 2.5 × 10?5 s?1. The UEL% and EL% reach to their maximum at the strain rate of 2.5 × 10?3 s?1. This phenomenon was explained by the observed grain structures and dislocation configurations. Whether or not the ductility can be enhanced with increasing strain rates depends on the competition between the homogenization of plastic deformation among the microconstituents (ultra-fine ferrite grains, relatively coarse ferrite grains as well as bainite) and the progress of cracks formed as a consequence of localized inconsistent plastic deformation. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|