Anodization of AZ91 magnesium alloy in alkaline solution containing silicate and corrosion properties of anodized films |
| |
Authors: | LI Ling-ling CHENG Ying-liang WANG Hui-min ZHANG Zhao |
| |
Affiliation: | [1]College of Materials Science and Engineering, Hunan University, Changsha 410082, China [2]Department of Chemistry, Zhejiang University, Hangzhou 310027, China |
| |
Abstract: | The anodization of AZ91 magnesium alloy in an alkaline electrolyte of 100g/L NaOH 20g/L Na2B4O7·10H2O 50g/L C6H5Na3O7·2H2O 60g/L Na2SiO3·9H2O was studied.The corrosion resistance of the anodized films was studied by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques.The microstructure of the films was examined with scanning electronic microscope (SEM) and X-ray diffractometer (XRD).The results show that,under the experimental conditions,the optimum anodizing time and the optimum anodizing current density are 40min and 20mA/cm2 respectively for obtaining the anodic film with high corrosion resistance.The XRD pattern shows that the components of the anodized film consist of MgO and Mg2 (SiO4). |
| |
Keywords: | AZ91 magnesium alloy anodized coating corrosion |
本文献已被 维普 万方数据 等数据库收录! |
|