The mechanical properties of carbon fibre reinforced Pyrex glass

The mechanical properties of carbon fibre reinforced Pyrex glass are discussed in terms of the volume fraction of fibre, the orientation of the fibres, fibre damage during fabrication, matrix porosity, matrix critical strain, interface properties and the mode of failure in bend tests. The stress at which matrix cracking occurs increases with fibre concentration indicating that the critical strain of the matrix increases as the fibre separation decreases. The ultimate strength of the composite is considerably greater than the stress at which the matrix begins to crack. Preliminary stress cycling experiments at stresses above that at which matrix cracks are formed suggest that propagation of these cracks is inhibited by the fibres.