| Zr55Al10Ni5Cu30块状非晶合金的高温压缩断裂 |
| |
| 引用本文： | 张庆生,张海峰,王爱民,丁炳哲,胡壮麒.Zr55Al10Ni5Cu30块状非晶合金的高温压缩断裂[J].金属学报,2002,38(8):835-838. |
| |
| 作者姓名： | 张庆生 张海峰 王爱民 丁炳哲 胡壮麒 |
| |
| 作者单位： | 中国科学院金属研究所沈阳材料科学国家,联合,实验室,沈阳,110016 |
| |
| 基金项目： | 国家重点基础研究发展规划 G2000067201，国家高技术研究发展计划 2001AA331010资助项目 |
| |
| 摘 要： | 利用Gleeble1500热模拟试验机研究了Zr55Al10Ni5Cu30块状非晶合金的高温压缩断裂，在室温情况下，在块状非晶合金断面的脉纹壁上出现了带有锯齿形边缘的裂口，在高温情况下，Zr55Al10Ni5Cu30块状非晶合金的宏观断面变得粗糙不平并出现了台阶，随着实验温度的不断上升，断面粘性流动特性变得更加明显，断面出现了大面积类似流动熔体凝固后的特征结构，塑性形变产生的最大剪切面的绝热温升或熔比是块状非晶合金中部粘性流动的原因。
|
| 关 键 词： | Zr55Al10Ni5Cu30块状非晶合金 高温压缩断裂 断口 绝热温升 |
| 文章编号： | 0412-1961(2002)08-0835-04 |
| 修稿时间： | 2001年12月18 |
COMPRESSION FRACTURE OF BULK Zr55Al10Ni5Cu30 AMORPHOUS ALLOY AT HIGH TEMPERATURE |
| |
| ZHANG Qingsheng,ZHANG Haifeng,WANG Aimin,DING Bingzhe,HU ZhuangqiShenyang National Laboratory for Materials Science.COMPRESSION FRACTURE OF BULK Zr55Al10Ni5Cu30 AMORPHOUS ALLOY AT HIGH TEMPERATURE[J].Acta Metallurgica Sinica,2002,38(8):835-838. |
| |
| Authors: | ZHANG Qingsheng ZHANG Haifeng WANG Aimin DING Bingzhe HU ZhuangqiShenyang National Laboratory for Materials Science |
| |
| Abstract: | The fracture behavior of bulk Zr55Al10Ni5Cu30 amorphous alloy under uniaxial compression at high temperature has been investigated. At room temperature, a crack with serrated edge appeared on the ridge of veins at the fracture surface for the bulk Zr55Al10Ni5Cu30 amorphous alloy. At high temperature, the compressive fracture surface of bulk Zr55Al10Ni5Cu30 amorphous alloy became much rougher than that at room temperature, and steps appeared on the fracture surface. With increasing the temperature, a different pattern from the vein appeared on the fracture surface at high temperature, which is very similar to the flowing-liquid solidified immediately. This type of fracture is most likely due to the adiabatic heating created by plastic flow. |
| |
| Keywords: | bulk Zr55Al10Ni5Cu30 amorphous alloy high temperature compression fracture fracture surface adiabatic heating |