Synthesis and tuning of ordering and crystallinity of mesoporous titanium dioxide film

Synthesis of well-organized and highly crystalline mesoporous titania (TiO₂) film is demonstrated using triblock copolymer (Pluronic P123) as a structure directing template, through the evaporation induced self-assembly (EISA) process. The issue of thermal and structural stability of a mesoporous TiO₂ film was addressed via optimization of annealing temperature and time. An anatase phase, high crystallinity TiO₂ film with ordered pores was obtained at 430 °C after annealing for 15 min. The synthesized film was crack free with TiO₂ nanoparticle size of 10–15 nm, quasi-hexagonal pore diameter in the range of 8–10 nm and film thickness of ~ 150 nm.