A novel technique for the development of acetabular cup by cold isostatic compaction and sintering of UHMWPE powder with optimized processing parameters

Life of a metal on ultra-high molecular weight polyethylene (UHMWPE) total hip replacement is often limited to 10–15 years, due to wear loss and aseptic loosening. Due to its high melt flow index, UHMWPE is typically processed by ram extrusion or compression molding technique, but yet to be processed to the full potential of its mechanical integrity in acetabular shape without any fusion defects or weak bonding. The main objective of the present study is to develop a novel technique to fabricate defect-free acetabular cups with desired bearing characteristics and surface finish by sintering medical-grade UHMWPE GUR 1050 powder after its cold isostatic compaction with optimum processing parameters. Sintering kinetics of UHMWPE is studied comprehensively using a thermomechanical analyzer. The influence of compaction pressure, sintering temperature, and sintering duration on sintering kinetics of UHMWPE is explored to realize their optimum. The optimally processed UHMWPE has the relative density of 97% and Vickers hardness of 5.4 with tensile yield strength and elastic modulus of 21.5 and 625 MPa, respectively. The newly developed acetabular cup exhibited inherent plateau-finished bearing surface with an average surface roughness of <100 nm, having good bearing characteristics and desired dimension.