The oxidation of two ternary Ni-Cu-10 at.% Al alloys in 1 atm of pure O2 at 800-900 °C

The oxidation of the ternary alloys Ni-45Cu-10Al and Ni-30Cu-10Al has been studied at 800-900 °C under 1 atm O₂. The presence of 10 at.% Al reduces significantly the oxidation rate of the corresponding Cu-Ni alloys during the initial oxidation stages, even before the establishment of a complete Al₂O₃ layer. The weight of individual sample of the two ternary Ni-Cu-10Al alloys at 800 °C increases more rapidly than at 900 °C during the initial oxidation stage. As oxidation proceeds, the weight gain at 800 °C slows down to a degree that the total weight gain after 24 h oxidation at 800 °C is less than that at 900 °C. Due to a faster formation of the Al₂O₃ layer, which suppresses earlier the further oxidation of Cu and Ni, the external region of the scales grown on Ni-45Cu-10Al contain much less Cu and Ni oxides than those grown on Ni-30Cu-10Al. The transition from the internal oxidation to the selective external oxidation of the most reactive component Al in Ni-Cu-Al alloys is favored by higher values of the Al content, of temperature and of the Cu/Ni ratio.