| 高温变换炉氢腐蚀原因分析及处理 |
| |
| 引用本文： | 周达理,陈飞鹏. 高温变换炉氢腐蚀原因分析及处理[J]. 大氮肥, 2003, 26(4): 228-230 |
| |
| 作者姓名： | 周达理 陈飞鹏 |
| |
| 作者单位： | 中石化股份公司巴陵分公司尿素产品部,湖南,岳阳,414003 |
| |
| 摘 要： | 高温变换炉在使用22年后产生了很严重的氢腐蚀鼓包缺陷。对高温变换炉氧腐蚀的原因进行分析，采取去氢及增加内隔热层等办法，有效地延长了该设备的使用寿命。
|
| 关 键 词： | 高温变换炉 氢腐蚀 鼓包缺陷 内隔热层 去氢 合成氨 |
| 修稿时间： | 2003-03-20 |
REASONS FOR HYDROGEN CORROSION OF THE HIGH TEMPERATURE SHIFT REACTOR AND THE TREATMENT |
| |
| Zhou Dali and Chen Feipeng. REASONS FOR HYDROGEN CORROSION OF THE HIGH TEMPERATURE SHIFT REACTOR AND THE TREATMENT[J]. Large Scale Nitrogenous Fertilizer Industry, 2003, 26(4): 228-230 |
| |
| Authors: | Zhou Dali and Chen Feipeng |
| |
| Abstract: | After twenty two years of operation,the high temperature shift reactor has generated serious failure caused by hydrogen corrosion This paper analyses the reason of the hydrogen corrosion of the high temperature shift reactor Measures such as hydrogen diffusing and adding inner insulating layer were taken which have extended the service life of this equipment effectively |
| |
| Keywords: | high temperature shift reactor hydrogen corrosion hydrogen diffusing inner insulating layer |