稀土对1Cr18Ni9钢腐蚀性能及组织状态影响 |
| |
引用本文: | 徐雳,石连升,王锐.稀土对1Cr18Ni9钢腐蚀性能及组织状态影响[J].高技术通讯,2001,11(8):102-104. |
| |
作者姓名: | 徐雳 石连升 王锐 |
| |
作者单位: | 1. 哈尔滨理工大学现代成型技术研究所 2. 哈尔滨工业大学应用化学系 |
| |
基金项目: | 863计划 (863 715 0 0 1 0 10 0 ),哈尔滨市学科后备带头人基金资助项目 (99712 180 0 5 ),G19990 3 3 0 |
| |
摘 要: | 利用化学法对1Cr18Ni9钢表面扩渗稀土,通过X-射线衍射分析了试样表面的组织状态。结果表明,1Cr18Ni9钢渗入稀土后,表面有CeFe7和LaO新相产生,并引起奥氏体含量降低,铁素体含量增加,改变了试样表面的微观结构。阳极极化曲线的测定结果表明,扩渗稀土后的1Cr18Ni9钢试样耐腐蚀性能超过了稳定化处理的1Cr18Ni9Ti钢水平。
|
关 键 词: | 稀土 1Cr18Ni9钢 组织状态 腐蚀性能 表面扩渗 奥氏体 微观结构 |
Influence of Rare-earths Gas-phase Permeation Treatment on the Surface Corrosion Resistance of 1Cr18Ni9 Steel |
| |
Abstract: | Rare earths was permeated on the surface of 1Cr18Ni9Ti steel by the chemical method. Then the composition and structure of the surface were investigated by the X ray diffraction. The results showed that after the treatment some new phases were formed, and austenite contents increased and ferrite contents decreased on the surface of 1Cr18Ni9 steel; Anode polarization test confirmed that its corrosion resistance exceeded that of stabilized 1Cr18Ni9Ti steel. |
| |
Keywords: | Rare earths 1Cr18Ni9 steel Structure states Corrosion resistance |