| 1Cr18Ni9Ti钢炉管开裂原因分析 |
| |
| 引用本文： | 李蓉蓉,李平瑾. 1Cr18Ni9Ti钢炉管开裂原因分析[J]. 理化检验(物理分册), 2009, 45(5): 292-298 |
| |
| 作者姓名： | 李蓉蓉 李平瑾 |
| |
| 作者单位： | 合肥通用机械研究院,合肥,230031 |
| |
| 摘 要： | 采用金相检验、力学性能试验、铁磁相含量测定、断口及能谱分析等方法对1Cr18Ni9Ti钢炉管的开裂原因进行分析。结果表明：开裂炉管的内壁裂纹为连多硫酸应力腐蚀开裂，而外壁裂纹为硫化物促进下的氯化物应力腐蚀开裂。并提出了预防炉管开裂的建议。
|
| 关 键 词： | 1Cr18Ni9Ti钢 炉管 连多硫酸 应力腐蚀开裂 |
Analysis on Cracking Reason of 1Cr18Ni9Ti Steel Furnace Tube |
| |
| LI Rong-rong,LI Ping-jin. Analysis on Cracking Reason of 1Cr18Ni9Ti Steel Furnace Tube[J]. Physical Testing and Chemical Analysis Part A:Physical Testing, 2009, 45(5): 292-298 |
| |
| Authors: | LI Rong-rong LI Ping-jin |
| |
| Affiliation: | Hefei General Machinery Research Institute;Hefei 230031;China |
| |
| Abstract: | The cracking reason of 1Cr18Ni9Ti steel furnace tube was analyzed by metallographic examination,mechanical performance test,ferrimagnetic phase content measurement,fractograph and EDS analysis etc.The results showed that there were PTA stress corrosion cracking on furnace tube inside wall and there were some stress corrosion cracking which was promoted by sulphide on furnace pipe outside wall.The proposal for avoiding cracking had been given. |
| |
| Keywords: | 1Cr18Ni9Ti steel furnace tube PTA stress corrosion cracking |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |