Effects of Ag addition on the microstructure and thermal stability of 6156 alloy |
| |
Authors: | Haifeng Zhang Ziqiao Zheng Yi Lin Xianfu Luo Jing Zhong |
| |
Affiliation: | 1.School of Material Science and Engineering,Central South University,Changsha,China |
| |
Abstract: | The effects of Ag addition on the microstructure and thermal stability of 6156 Al–Mg–Si–Cu alloy were investigated by means
of hardness measurement, tensile tests, differential scanning calorimetry, and transmission electron microscopy. The results
showed that addition of small amount of Ag to 6156 alloy did not change the precipitation sequence mainly β″ and Q′ strengthening phase but slightly accelerated the age-hardening rate and increased peak hardness at the same aging condition.
The tensile properties enhanced about 30 MPa at the room temperature or thermal exposure at lower temperature (<100 °C). With
the exposed temperature and time increased to 150 °C for 1000 h, almost no difference between the Ag-containing and Ag-free
alloys. When exposed at 200 °C, the tensile strength of Ag-containing alloy became lower than that of Ag-free alloy because
of the coarsening precipitations in matrix and boundary observed by TEM observed. For both alloys, thermal exposure at temperatures
100 °C for long time periods had no significant effect on tensile properties. Loss in strength was small and large with prolonging
the exposure time at 150 and 200 °C, respectively. |
| |