Microstructural evolution during controlled ball milling of (Mg2Ni+MgNi2) intermetallic alloy

Nearly dual-phase Mg–Ni alloy fabricated by ingot metallurgy (IM) and comprising 30 vol% Mg₂Ni and 61 vol% MgNi₂ intermetallic compounds (remaining 9 vol% of unreacted Mg) was mechanically (ball) milled under controlled shearing for 10, 30, 70 and 100 h. The majority of the medium- and small-sized powder particles exhibited a relatively homogeneous microstructure of milled Mg₂Ni and MgNi₂. A fraction of large-sized particles developed the ‘core and mantel’ microstructure after milling for 70 and 100 h. The ‘core’ contains poorly milled MgNi₂ particles and the ‘mantel’ is a thoroughly milled mixture of Mg₂Ni, MgNi₂ and, possibly, residual Mg. X-ray diffraction provides evidence of nanostructurization and eventual amorphization of a fraction of a heavily ball milled Mg₂Ni phase. The remnant Mg₂Ni developed a nanocrystalline/submicrocrystalline structure. The co-existing MgNi₂ phase developed a submicrocrystalline structure within the powder particles. The results are rationalized in terms of enthalpy effects by the application of Miedema’s semi-empirical model to the phase changes in ball milled intermetallics.