Study on Sensitizing Technology of Emulsion Explosive Sensitized by Resin Microspheres
XIE Shengyan,HE Junrong,XIAO Jinglong,LI Yang,LUO Dawu,LUO Yangwei. Study on Sensitizing Technology of Emulsion Explosive Sensitized by Resin Microspheres[J]. Explosive Materials, 2018, 47(1): 26-31. DOI: 10.3969/j.issn.1001-8352.2018.01.005
Authors:XIE Shengyan  HE Junrong  XIAO Jinglong  LI Yang  LUO Dawu  LUO Yangwei
Abstract:Status of sensitizing technology of emulsion explosives was compared. Resin microspheres were proposed to be used as a good physical sensitizer in preparation of emulsion explosive. Sensitizing performance of emulsion explosive sensitized by resin micro spheres was evaluated in terms of density, blasting performance, viscosity, pumping stability and storage stability in test. The results show that when the mass fraction of the resin microsphere is 0. 35%-0. 45%, the density of the emulsion explosive prepared is 1. 09-1. 15 g/cm3 , the detonation velocity is 5200-5400m/s and the gap distance is 6-9 cm;at high temperature of 80℃, the viscosity of emulsion explosive sensitized by resin microsphere is slightly higher than that of the emulsion explosive sensitized chemically, and it is far less than that of emulsion explosive sensitized by expanded perlite;the pumping stability of the emulsion explosive sensitized by resin microsphere is superior to the emulsion explosive sensitized by chemical method and expanded perlite.