| Abstract: | Epitaxial Ba0.6Sr0.4TiO3 (BST) thin films were deposited on LaAlO3 (LAO) substrates with the conductive metallic oxide La0.5Sr0.5CoO3 (LSCO) film as a bottom electrode by pulsed laser deposition (PLD). Xray relationship of BST/LSCO/LAO was 001] BST//001]LSCO//001] LAO. The atomic force microscope (AFM)revealed a smooth and crackfree surface of BST films on LSCOcoated LAO substrate with the average grain size of 120 nm and the RMS of 1.564 nm for BST films.Pt/BST/LSCO capacitor was fabricated to perform CapacitanceVoltage measurement indicating good insulating characteristics. For epitaxial BST film, the dielectric constant and dielectric loss were determined as 471 and 0.03, respectively. The tunabilty was 79.59% and the leakage current was 2.63×107 A/crm2 under an applied filed of 200 kV/cm. Furthermore, it was found that epitaxial BST (60/40) films demonstrate wellbehaved ferroelectric properties with the remnate polarization of 6.085 μC/cm2 and the coercive field of 72 kV/cm. The different electric properties from bulk BST (60/40)materials with intrinsic paraelectric characteristic are attributed to the interface effects. |