Combinatorial preparation and high-throughput catalytic tests of multi-component deNOx catalysts

A quaternary catalyst library of 56 samples comprising all combinations of four elements, viz. Ag, Co, Cu, In, with six equally spaced atomic fraction increments from 0 to 1 was prepared by impregnation of a proprietary mesoporous alumina support. Catalytic properties of the library were tested in the selective catalytic reduction (SCR) of NO_x by propane under lean conditions in the temperature range 400–500 °C. The catalytic data acquired by a parallel 64-channel microreactor system with automated time-of-flight mass spectrometric analysis have been evaluated regarding selectivity–compositional relationships, synergistic effects for NO_x conversion, and efficiency of propane utilization. Full conversion of NO_x is achieved over Ag–Co combinations at 450 °C with N₂ selectivities of more than 90% and reductant utilization of 20% in a feed of 1500 ppm NO, 1500 ppm propane and 5 vol.% O₂ (space velocity of 36,000 cm³ g_cat^?1 h^?1). For the single-component catalysts Ag/Al₂O₃, Co/Al₂O₃, Cu/Al₂O₃, and In/Al₂O₃, the state of the elements on the mesoporous alumina was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Cobalt forms a spinel-like cobalt aluminate phase whereas copper and indium are present as oxides with small sizes not detectable by XRD. Silver occurs in both metallic state and as Ag₂O, and forms Ag_n clusters of at least two different sizes, predominantly with diameters of about 30 nm. The conclusions are consistent with the reducibility of the single-component catalysts samples by H₂. Surface area measurements and pore size distributions revealed reasonable modifications of the textural properties. The main pore size of the alumina support is decreased from 7 to ca. 5 nm after loading of the active components.