Effects of corrosive environments on near-threshold fatigue crack growth behavior of T1-6A1-4V

The near-threshold fatigue crack growth behavior of Ti-6A1-4V alloy has been investigated in low O₂ steam (< 1 ppm), high O₂ steam (40ppm), and boiling water with various concentrations of Nad and/or Na₂₂SO₄. At load ratio (R) of 0.5, high O₂ steam increased the crack propagation rates in the threshold region, relative to low O₂ steam. However, at R = 0.8, the near-threshold crack growth rates in low and high O₂ steam were comparable. Values of threshold stress intensity range, ΔK_th, slightly increased with an increase in the concentration of NaCl in the solution. Varying solution pH from 5.0 to 10.0 in a 0.1 g NaCl plus 0.1 g Na₂SO₄ per 100ml H₂O solution had no effect on the rates of near-threshold crack propagation. Increasing the hydrazine level from 30 to 10⁷ ppb in the same salt solution also did not change the resistance to crack growth. Comparing the present results with the previous data on 403 stainless steel, the near-threshold crack propagation rate performance in Ti-6Al-4V alloy is superior to that in 403 steel in both the steam and salt solution environments.