The formation of CuInSe2 thin film solar cell absorbers from electroplated precursors with varying selenium content

We present results from real-time X-ray diffraction experiments on the formation of CuInSe₂ solar cell absorbers by annealing precursors, produced by simultaneous electrodeposition of copper, indium and selenium. The investigations reveal, that a reduced amount of electrochemically deposited selenium is the decisive parameter in order to realise a chalcopyrite formation behaviour as observed for sputtered stacked elemental layer (SEL) precursors. A simultaneous electrodeposition of the elements copper, indium and selenium in the molar ratio 1:1:2 of the chalcopyrite CuInSe₂ leads to the formation of binary copper and indium selenides during the electrodeposition process. The existence of binary selenides besides the intermetallic phase Cu₁₁In₉ as initial phases leads to an unfavourable absorber morphology. This can be explained by the observed semiconductor formation mechanism. A reduction of the deposited amount of selenium favours the formation of the intermetallic compound Cu₁₁In₉ and reduces the amount of binary selenides. These precursors show a formation behaviour and resulting absorber morphology as known for sputtered SEL precursors.