The stress-whitened damage zone of PVC blends

The stress-whitened damage zone that formed ahead of a semicircular notch during slow tensile loading has been measured from optical micrographs of translucent blends of poly(vinyl chloride) (PVC) with experimental chlorinated polyethylene (CPE) resins. When the zone was small, the plane strain condition applied and from the elastic stress distribution a constant mean stress condition was found at the boundary of the crescent-shaped zone. The critical mean stress did not depend on the chlorine content or the chlorine distribution of the experimental CPE resin used in the blend. While the critical mean stress decreased as the amount of CPE in the blend was increased, the critical volume strain, calculated from the bulk modulus, was independent of composition and was thought to be the controlling parameter for stress-whitening. When the zone was larger, the shape was qualitatively described by concepts of stress redistribution in the presence of a plastic zone ahead of the notch. Macroscopic flow and necking were only detected near the maximum in the stress-displacement curve.