Bulk WC-Al2O3 composites prepared by spark plasma sintering

WC and WC-Al₂O₃ materials without metallic binder addition were densified by spark plasma sintering in the range of 1800-1900 °C. The densification behavior, phase constitution, microstructure and mechanical properties of pure WC and WC-Al₂O₃ composite were investigated. The addition of Al₂O₃ facilitates sintering and increases the fracture toughness of the composites to a certain extent. An interesting phenomenon is found that a proper content of Al₂O₃ additive helps to limit the formation of W₂C phase in sintered WC materials. The pure WC specimen possesses a hardness (HV₁₀) of 25.71 GPa, fracture toughness of 4.54 MPa·m^1/2, and transverse fracture strength of 862 MPa, while those of WC-6.8 vol.% Al₂O₃ composites are 24.48 GPa, 6.01 MPa·m^1/2, and 1245 MPa respectively. The higher fracture toughness and transverse fracture strength of WC-6.8 vol.% Al₂O₃ are thought to result from the reduction of W₂C phase, the crack-bridging by Al₂O₃ particles and the local change in fracture mode from intergranular to transgranular.