Correlation between the cyclic stress behavior and microstructure in 316LN based on the analysis of hysteresis loops |
| |
Authors: | Bo Chang Zheng Zhang |
| |
Affiliation: | 1. School of Materials Science and Engineering, Beihang University, Beijing, 100191, China
|
| |
Abstract: | Total strain controlled cyclic test was performed on 316LN under uniaxial loadings. Through the partitioning of hysteresis loops, the evolution of two components of cyclic flow stress, the internal and effective stresses, was reported. The former one determines the cyclic stress response. Based on the transmission electron microscopic (TEM) observation on specimens loaded with scheduled cycles, it is found that planar dislocation structures prevail during the entire cyclic process at low strain amplitude, while a remarkable dislocation rearrangement from planar structures to heterogeneous spatial distributions is companied by a cyclic softening behavior at high strain amplitude. The competition between the evolution of the intergranular and the intragranular components of the internal stress caused by the transition of slip mode induces the cyclic hardening and softening at high strain levels. The intergranular internal stress represents the most part of the internal stress at low strain level. |
| |
Keywords: | cyclic stress behavior partitioning of hysteresis loops microstructure dislocation rearrangement internal stress |
本文献已被 CNKI 维普 SpringerLink 等数据库收录! |
|