Alternative-Ultrathin Assembling of Exfoliated Manganese Dioxide and Nitrogen-Doped Carbon Layers for High-Mass-Loading Supercapacitors with Outstanding Capacitance and Impressive Rate Capability

Manganese dioxide (MnO₂) materials have received much attention as promising pseudocapacitive materials owing to their high theoretical capacitance and natural abundance. Unfortunately, the charge storage performance of MnO₂ is usually limited to commercially available mass loading electrodes because of the significantly lower electron and ion migration kinetics in thick electrodes. Here, an alternatively assembled 2D layered material consisting of exfoliated MnO₂ nanosheets and nitrogen-doped carbon layers for ultrahigh-mass-loading supercapacitors without sacrificing energy storage performance is reported. Layered birnessite-type MnO₂ is efficiently exfoliated and intercalated by a carbon precursor of dopamine using a fluid dynamic-induced process, resulting in MnO₂/nitrogen-doped carbon (MnO₂/C) materials after self-polymerization and carbonization. The alternatively stacked and interlayer-expanded structure of MnO₂/C enables fast and efficient electron and ion transfer in a thick electrode. The resulting MnO₂/C electrode shows outstanding electrochemical performance at an ultrahigh mass loading of 19.7 mg cm⁻², high gravimetric and areal capacitances of 480.3 F g⁻¹ and 9.4 F cm⁻² at 0.5 mA cm⁻², and rapid charge/discharge capability of 70% capacitance retention at 40 mA cm⁻². Furthermore, asymmetric supercapacitor based on high-mass-loading MnO₂/C can deliver an extremely high energy of 64.2 Wh kg⁻¹ at a power density of 18.8 W kg⁻¹ in an aqueous electrolyte.