| STUDY OF PREPARATION PROCESS OF TUNGSTEN POWDER BY SHS WITH A MAGNESIUM THERMIT STAGE |
| |
| 引用本文： | T.A.Zhang Y.L.Wang Z.H.Dou H.Yang. STUDY OF PREPARATION PROCESS OF TUNGSTEN POWDER BY SHS WITH A MAGNESIUM THERMIT STAGE[J]. 金属学报(英文版), 2004, 17(5): 719-724 |
| |
| 作者姓名： | T.A.Zhang Y.L.Wang Z.H.Dou H.Yang |
| |
| 作者单位： | [1]SchoolofMetallurgy＆Materials,NortheasternUniversity,Shenyang110004,China [2]InstituteofMetalResearch,TheChineseAcademyofSciences,Shenyang110016,Ghina |
| |
| 摘 要： | Tungsten powder was fabricated from the system CaWOrMg by self-propagating high-temperature synthesis (SHS) with a magnesium thermit stage. The physic-chemical change during heating and the effects of pressure of sample and diluents (W powder) on product have been studied. The experimental results show that the porosity of combustion product and the particle size of final tungsten powder decrease with increasing pressure of sample. Addition of diluents could increase the particle size of final tungsten powder. The purity of tungsten is improved by leaching in NaOH solution. The results of spectral analysis and particle size distribution of final tungsten powder show that the final Tungsten powder has a median diameter of 0.87μm, specific surface area of 1.09m^2/g and purity of above 99.0%.
|
| 关 键 词： | SHS 自传播高温合成工艺 镁 铝热剂 钨粉 熔点 合金 |
STUDY OF PREPARATION PROCESS OF TUNGSTEN POWDER BY SHS WITH A MAGNESIUM THERMIT STAGE |
| |
| T.A.Zhang,Y.L.WANG,Z.H.Dou,H.Yang. STUDY OF PREPARATION PROCESS OF TUNGSTEN POWDER BY SHS WITH A MAGNESIUM THERMIT STAGE[J]. Acta Metallurgica Sinica(English Letters), 2004, 17(5): 719-724 |
| |
| Authors: | T.A.Zhang Y.L.WANG Z.H.Dou H.Yang |
| |
| Affiliation: | School of Metallurgy＆Materials,Northeastern University,Shenyang110004,China |
| |
| Abstract: | Tungsten powder was fabricated from the system CaWO4-Mg by self-propagating high-temperature synthesis (SHS) with a magnesium thermit stage. The physic-chemical change during heating and the effects of pressure of sample and diluents (W powder) on product have been studied. The experimental results show that the porosity of combustion product and the particle size of final tungsten powder decrease with increasing pressure of sample. Addition of diluents could increase the particle size of final tungsten powder. The purity of tungsten is improved by leaching in NaOH solution. The results of spectral analysis and particle size distribution of final tungsten powder show that the final Tungsten powder has a median diameter of 0.87μn, specific surface area of 1.09m2/g and purity of above 99.0%. |
| |
| Keywords: | self-propagating high-temperature synthesis (SHS) magnesium thermit tungsten Powder |