Production of Al–Ti–B master alloys from Ti sponge and KBF4

It is of great interest to replace the K₂TiF₆ salt so as to reduce the volume of fluoride-bearing particulate material to be added to the aluminium melt in the popular “halide salt” process. Ti sponge was used in the present work as the source of Ti in the production of an Al–5Ti–1B grain refiner. Addition of Ti granules into molten aluminium, either premixed with or before KBF₄ salt, has produced Al–5Ti–1B alloys where the boride particles were relatively few and predominantly of the AlB₂ type. The grain refining efficiency of these alloys were far from satisfactory. TiB₂ was the dominant boride phase with sufficient number of blocky aluminide particles when Ti, in excess of the TiB₂ stoichiometry was supplied before hand and the balance was reserved for co-addition with KBF₄. Al₃Ti particles were generated soon after the Ti solubility limit was exceeded in the first step while the boride particles were subsequently produced by the reaction between molten aluminium, KBF₄ and K₂TiF₆. The Al–5Ti–1B master alloy thus produced provided an adequate grain refining performance while the amount of particulate material to be added to the aluminium melt was reduced by nearly 30%.