Bestimmung der Abtragungsraten von Zirconium,Tantal und der Legierung Tantal-40Niob in fluoridhaltiger azeotroper Salpetersäure mit Hilfe der Radiotracer-Methode

The radiotracer technique as a means to investigate the corrosion of zirconium, tantalum, and a Ta-40Nb alloy in fluoride containing azeotropic nitric acid Zirconium and tantalum as well as the tantalum 40% niobium alloy are of considerable technical importance due to their high corrosion resistance against numerous corrosive media. With respect to corrosion testing in analytically pure azeotropic nitric acid in the temperature range between 20 and 121°C, corrosion rates were determined for zirconium: 7 · 10^?6 to 5 · 10^?4 mm/y, for tantalum: 10^?8 to 4 · 10^?6 mm/y, and for the Ta-40Nb alloy: 2 · 10^?7 to 8 · 10^?6 mm/y 1]. These corrosion rates will be markedly increased by adding small amounts of fluorides or by fluoride impurities. The radiotracer method after neutron activation was applied to determine the corrosion rates in azeotropic fluoride containing nitric acid. Even minute additions of fluorides strongly affect the corrosion resistance of zirconium. In the range between 0.15 and 10 ppm F^? and at a temperature of 108°C, corrosion rates between 5.3 · 10^?3 and 3.1 mm/y were measured. It was impossible to establish a limit for the fluoride concentration, below which the corrosion rate of zirconium will not be adversely influenced. The corrosion rates of tantalum and the Ta-40Nb alloy are considerably increasing above a fluoride concentration of 10 ppm. The highest corrosion rates measured were between 8.4 · 10^?3 mm/y at 50°C/280 ppm F^? and 1.4 · 10^?2 mm/y at 110°C/320 ppm F^?. Within the range of this investigation, the corrosion resistance of tantalum was higher than that of the Ta-40Nb alloy by one order of magnitude. The corrosion resistance of zirconium and tantalum was not influenced by any treatment of the samples before testing.