Kinetics of sol-to-gel transition for poloxamer polyols

Kinetics of gelation for aqueous solutions of poloxamers 407 and 288 were determined using pulse shearometry. The principle of this method for determining the shear modulus of a semisolid was based on generation of a torsional force that is transmitted through the poloxamer sample at discrete time intervals. Three distinct linear phases were observed for the log dynamic shear modulus (G′) vs. time profiles as poloxamer 407 and 288 solutions of varying concentrations were allowed to passively warm at room temperature to a temperature exceeding the sol-to-gel transition temperature, T_m. The beginning of the second exponential phase coincided with the onset of the gelation process as determined by visual observation. Although gelation appeared visually to be complete at the beginning of the third exponential phase of the log G′ vs. time profiles, this last exponential phase may indicate the rate of formation of the polymer network. A comparison of poloxamer 407 30% (w/w); T_m = 10.9°C] and poloxamer 288 37% (w/w); T_m = 11.1°C] would suggest that the concentration of poloxamer required to achieve approximately the same gelation temperature for poloxamers having a similar ratio of poly(oxypropylene):poly(oxyethylene) units decreases with increasing molecular weight of the poly(oxypropylene) hydrophobe contained in the copolymer. Results of these preliminary studies suggest that the gelation process was significantly (p < .05) more rapid for poloxamer 407 at a 30% (w/w) concentration compared to a 30% (w/w) solution of poloxamer 288 when the poloxamer solutions were allowed to passively warm at room temperature. In addition, it appears that the rate of gelation for the poloxamer solutions studied was dependent on the rate of heat transfer through the polymer solution.