Silver (Ag) as a novel masking material in glass etching for microfluidics applications |
| |
Authors: | Hing Wah Lee Daniel C. S. Bien Siti Aishah Mohamad Badaruddin Aun Shih Teh |
| |
Affiliation: | 1. MEMS/NEMS Cluster, MIMOS BERHAD, Technology Park Malaysia, Kuala Lumpur, Malaysia
|
| |
Abstract: | In this paper, we report the use of a single masking film for deep glass etching in hydrofluoric acid (HF). Thin film silver (Ag) is the key masking material in this work enabling a simple and low cost fabrication of microfluidic structures. The Ag film was deposited by evaporation and etched in a diluted nitric acid and de-ionized water solution at a ratio of 1:3. Surface morphology for different thicknesses of Ag film and its correlation to the maximum achievable etch depth is analyzed. AFM results shows low roughness values (<5 nm), indicating the Ag films are of smooth surface. With a 100 nm Ag film, a 220 μm etch depth in borosilicate glass substrates were produced and by further thickening the Ag to 300 nm, etch depths exceeding 300 μm were successfully achieved. SEM images show that thinner Ag films are of finer grains, potentially a source for pinholes formation where rapid penetration of HF along the grain boundaries peels off the Ag film from the glass surface. However, the Ag film was found not to react with HF. The process was demonstrated in the fabrication of cavities for integration with other microfluidic devices. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|