Bonding of Silicon Nitride Ceramic Composite with RE 2O 3 Al 2O 3 SiO 2 Glass Solders |
| |
| Zhou Fei.Bonding of Silicon Nitride Ceramic Composite with RE 2O 3 Al 2O 3 SiO 2 Glass Solders[J].Journal of Rare Earths,1999(3). |
| |
| Authors: | Zhou Fei |
| |
| Abstract: | Liquid bonding of Si 3N 4 ceramic composite was carried out with RE 2O 3 Al 2O 3 SiO 2 glass solders. The effect of bonding conditions and interfacial reaction on the joint strength was studied. The joint strength under different bonding conditions was measured by four point bending tests. The interfacial microstructures were observed and analyzed by SEM, EPMA and XRD. It is shown that the liquid glass solders react with Si 3N 4 at interface, forming the Si 3N 4/Si 2N 2O/Y(La) sialon glass/Y(La) sialon glass gradient interface. With the increase of bonding temperature and holding time, the joint strength first increased reaching a peak, and then decreased. According to microanalyses, LaYO 3 precipitated from joint glass improves joint strength at room and high temperature. |
| |
| Keywords: | Rare earths Si 3N 4 ceramic composite Lanthana Yttria Bonding |
|