Unperturbed dimension of poly(4-acetoxystyrene) measured in good and theta solvents

In order to obtain the additional data concerning the unperturbed dimension of poly-4-substituted styrene, light scattering measurements are performed on the twenty-two fractions with molecular weight of (0.91–352)·10⁴ of poly(4-acetoxystyrene) in dioxan at 25°C, from which the molecular weight obtained was found easily to be evaluated with the gel permeation chromatography using THF. Phase separation experiments for this polymer indicate that the theta state is attained in isopropyl acetate at 19.7°C and butyl acetate at 26.8°C. By making viscosity measurements at that state, the value of K_Θ is directly evaluated as 5.4·10^?4 dl g^?1. The limiting viscosity number is also obtained in good solvents, THF and dioxan, at 25°C and constants of the Mark-Houwink-Sakurada equation in each solvent are determined. Further, approximately the same K_Θ as above is obtained from these data with the Stockmayer-Fixman plot. The calculated value of steric factor, 2.37, on this polymer may be plausible, compared with those of polyvinylaromatic derivatives.