Poly(arylene ether sulfone) multi-block copolymers bearing perfluoroalkylsulfonic acid groups

Poly(arylene ether sulfone) (PAES) multi-block copolymers bearing perfluoroalkylsulfonic acid moieties were prepared from hydrophilic and hydrophobic prepolymers. The latter were synthesized by reaction of N,N-diisopropylethylammonium 2,2-bis(p-hydroxyphenyl)pentafluoropropanesulfonate (HPPS) with bis-(4-fluorophenyl) sulfone (FPS), and biphenol (BP) with FPS, respectively. Prepolymers and multi-block copolymers were prepared at 180 °C in N,N-dimethylacetamide in the presence of K₂CO₃. The prepolymers were reacted overnight; the multi-block copolymers were reacted only 80 min to minimize transetherification. Prepolymers and multi-block copolymers were characterized using ¹H and ¹³C NMR. ¹⁹F NMR provided molecular weight of hydrophilic prepolymers bearing aryl fluoride end groups. GPC was used to characterize the multi-block copolymers. Copolymer block lengths were determined by quantifying ¹³C NMR peak areas of quaternary carbon atoms adjacent to sulfur in FPS moieties. Hydrophilic and hydrophobic block lengths were in the range 9.4-23.4 and 4.4-11.8 repeating units, respectively. AFM showed phase separation for all block lengths. Conductivity at 80 °C and 100% relative humidity ranged from 6.2 to 34.3 mS/cm, with the best value obtained for hydrophilic/hydrophobic block lengths of 13.3/6.0.