Dynamically confined crystallization in a soft lamellar space constituted by alternating polymer co-brushes

Crystallization kinetics and behavior of PCL side chains in polymer co-brushes constituted with PCL and PEO side chains alternatively attached on poly(styrene-alt-maleimide) backbones have been determined using in-situ FT-IR and DSC methods. Avrami analysis shows the exponent n increasing from one at 10 °C to two at 30 °C, demonstrating confined crystallization of PCL side chains through homogeneous or heterogeneous nucleation. PLM morphological characterization displays typical spherulites of which size is dependent on the crystallization temperature and further AFM visualization shows typical PCL lamellae at 30 °C and broken lamellae at 10 °C embedded within PEO + backbone matrix inside of spherulites. Such lamellar structure explains the confined crystallization with Avrami exponent n ≤ 2. Formation of the broken lamellae can further clarify the reason why Avrami exponent decreases to n ≈ 1 at 10 °C, that is, homogeneous nucleation in the isolated crystals. Dynamically confined crystallization has been proposed based on their special molecular architecture. Comparing to statically confined crystallization, the construction of confined space and the crystallization process were almost synchronous. The formation of spherulites mesoscopically reveals the entire molecule motion and assembly through a pathway of conventional crystalline polymers and the crystallization of PCL side chains in a space constituted by stiff backbones of poly(styrene-alt-maleimide) plus soft PEO layer microscopically reflects a confined character which has been observed in some conventional block copolymers.