Recovery of neutron-irradiation-induced defects of Al2O3, Y2O3, and yttrium-aluminum garnet |
| |
Authors: | Toyohiko Yano Hiroshi Konishi Saishun Yamazaki Mohd Idzat bin Idris Katsumi Yoshida |
| |
Affiliation: | 1. Laboratory for Advanced Nuclear Energy, Institute of Innovative Research, Tokyo Institute of Technology, O-okayama, Meguro-ku, Tokyo, Japan;2. Department of Nuclear Engineering, Tokyo Institute of Technology, O-okayama, Meguro-ku, Tokyo, Japan;3. The National University of Malaysia, School of Applied Physics, Faculty of Science and Technology, Bangi Selangor, Malaysia |
| |
Abstract: | SiC fiber-reinforced SiC matrix composites (SiCf/SiC) are considered as one of the candidates for blanket materials in future fusion reactors and as an advanced fuel cladding material for next-generation fission reactors. Generally, the densification of SiC needs sintering additives and oxides such as Al2O3, Y2O3, and yttrium-aluminum garnet (YAG, Y3Al5O12), which are frequently added to SiC. However, the effects of neutron irradiation on sintering additives are still unclear. In this study, we performed the neutron irradiation of Al2O3, Y2O3, and YAG at fluences up to 2.0–2.5 × 1024 n/m2 (E > 0.1 MeV) at 60–90 °C. The isochronal recovery of the macroscopic volume of Al2O3 against annealing temperature showed smooth and continuous shrinkage at a temperature of up to 1200 °C, and the volume slightly increased above that temperature. In contrast, the volume of Y2O3 showed quick shrinkage at the low temperature range, and slower and smooth recovery was observed up to ~1100 °C. In the case of YAG, the recovery of volume occurred in a step-wise manner at 600–750 °C, and continuous shrinkage occurred at temperatures lower and higher than that temperature range. The activation energies for the macroscopic volume recoveries of three oxides were obtained from the Arrhenius plots of the rate coefficients. Two-stage recovery was observed for Al2O3, whereas more complicated recovery processes were suggested for Y2O3 and YAG. |
| |
Keywords: | Al2O3, Y2O3 yttrium-aluminum garnet (YAG) neutron irradiation defect recovery activation energy |
|
|