随焊冲击碾压整形新方法及等承载接头拉伸与疲劳性能
引用本文:王佳杰,杨建国,张敬强,董志波,方洪渊,刚铁. 随焊冲击碾压整形新方法及等承载接头拉伸与疲劳性能[J]. 焊接学报, 2012, 33(11): 35-38
作者姓名:王佳杰  杨建国  张敬强  董志波  方洪渊  刚铁
作者单位:1. 哈尔滨工业大学先进焊接与连接国家重点实验室,哈尔滨150001 黑龙江工程学院材料与化学工程学院,哈尔滨150050
2. 浙江工业大学化工机械设计研究所,杭州,310014
3. 哈尔滨工业大学先进焊接与连接国家重点实验室,哈尔滨,150001
基金项目:中俄政府间科技合作资助项目
摘    要:提出了随焊冲击碾压整形方法(weld shaping with trailing impact rolling,,WSTIR),并研制了一套随焊冲击碾压整形装置.对随焊整形后低匹配等承载接头(equal load-carrying capacity,ELCC)进行了拉伸试验和疲劳试验.结果表明,随焊整形后接头拉伸均断裂在近焊趾的母材处,断裂应力均达到母材的抗拉强度;随焊整形后接头的疲劳寿命明显大于原始焊态接头,由于随焊整形接头焊趾处圆弧过渡降低了应力集中,进而提高了随焊整形接头的疲劳承载能力.拉伸与疲劳试验说明随焊冲击碾压整形后的平余高低匹配接头达到了等承载的要求.这种随焊整形方法将有力地推动低匹配等承载接头设计方法在工程实际的应用.

关 键 词:低匹配对接接头  随焊冲击碾压整形  拉伸性能  疲劳性能
收稿时间:2012-08-06

A new weld shaping method with trailing impact rolling and tensile and fatigue properties for equal load-carrying capacity joints
WANG Jiajie,YANG Jianguo,ZHANG Jingqiang,DONG Zhibo,FANG Hongyuan and GANG Tie. A new weld shaping method with trailing impact rolling and tensile and fatigue properties for equal load-carrying capacity joints[J]. Transactions of The China Welding Institution, 2012, 33(11): 35-38
Authors:WANG Jiajie  YANG Jianguo  ZHANG Jingqiang  DONG Zhibo  FANG Hongyuan  GANG Tie
Affiliation:State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China;School of Materials and Chemical Engineering, Heilongjiang Institute of Technology, Harbin 150050, China,Institute of Process Equipment and Control Engineering, Zhejiang University of Technology, Hangzhou 310014, China,State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China,State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China,State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China and State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China
Abstract:A new modified technology is put forward in which weld shaping with trailing impact rolling is used(WSTIR).The integrated device of WSTIR has also been designed.Tensile test and fatigue test has been carried out respectively for under-matched equal load-carrying capacity joints after modifying.Tensile test results show that tensile fracture occurs in the base metal near the weld toe and tensile strength reaches the tensile strength of base metal for equal load-carrying capacity joints after WSTIR.Fatigue test results show that the fatigue life of equal load-carrying capacity joints after WSTIR is significantly greater than the original welded joints.The weld toe arc transition can reduce stress concentration, thereby improve fatigue carrying capacity of WSTIR joints.The results of tensile and fatigue test show that the modified flat-reinforcement joints have the same load carrying capcity with base metal.This shaping method with WSTIR will greatly promote the practical application in engineering for the undermatching equal load-carrying capacity joints.
Keywords:undermatching welded joints  weld shaping with trailing impact rolling  tensile property  fatigue property