Hydrogen generation by hydrolysis of sodium borohydride on CoB/SiO2 catalyst

Generation of hydrogen by hydrolysis of alkali metal hydrides has attracted attention. Unsupported CoB catalyst demonstrated high activity for the catalytic hydrolysis of NaBH₄ solution. However, unsupported CoB nanoparticles were easy to aggregate and difficult to reuse. To overcome these drawbacks, CoB/SiO₂ was prepared and tested for this reaction. Cobalt (II) acetate precursor was loaded onto the SiO₂ support by incipient-wetness impregnation method. After drying at 100 °C, Co cations were deposited on the support. The dried sample was then dispersed in methanol/water solution and then fully reduced by NaBH₄ at room temperature. The catalyst was characterized by N₂ sorption, XRD and XPS. The results indicated that the CoB on SiO₂ possessed amorphous structure. B and Co existed both in elemental and oxidized states. SiO₂ not only affected the surface compositions of CoB, but also affected the electronic states of Co and B. B⁰ could donate partial electron to Co⁰. The structure effect caused by the SiO₂ support helped to prevent CoB nanocluster from aggregation and therefore the activity increased significantly on hydrolysis of alkaline NaBH₄ solution. The CoB/SiO₂ catalyst showed much higher activity than the unsupported CoB catalyst. At 298 K, the hydrogen generation rate on CoB/SiO₂ catalyst was 4 times more than that on the unsupported CoB catalyst. The hydrogen generation rate was as high as 10,586 mL min⁻¹ g⁻¹ catalyst at 298 K. CoB/SiO₂ is a very promising catalyst for this reaction.