Changing Rule of Carbon-Enriched Zone and Diffusion Behavior of Carbon in Aging 0Cr6Mn13Ni10MoTi/1Cr5Mo Dissimilar Welded Joints |
| |
Authors: | Zheng LIU Ligang WANG Lai WANG |
| |
Affiliation: | Department of Materials Engineering, Dalian University of Technology, Dalian 116024,China |
| |
Abstract: | The microstructures, the changing rule of carbon-enriched zone, the diffusion behaviors of elements C and Cr, and the carbide type of 0Cr6Mn13Ni10MoTi/1Cr5Mo dissimilar welded joints after aging at 500℃ for various times and after long-term service in technical practice were investigated by using the optical microscopy, electron probe microanalysis, scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that in aging 0Cr6Mn13Ni10MoTi/1Cr5Mo dissimilar welded joints, the main carbides are M3C and a few carbides are M7C3 and M23C6. The M3C carbide decomposition and dissolution with increasing aging time or aging temperature and the anti-diffusion of C and Cr cause the decrease and disappearance of the carbon-enriched zone. The results are different from those of the A302/1Cr5Mo dissimilar welded joints in previous studies. |
| |
Keywords: | Dissimilar welded joint Aging Diffusion Carbides |
本文献已被 CNKI 万方数据 等数据库收录! |
| 点击此处可从《材料科学技术学报》浏览原始摘要信息 |
|
点击此处可从《材料科学技术学报》下载全文 |
|