Mechanism of Slag Composition Change During Electroslag Remelting Process |
| |
Authors: | ZHAO Jun-xue CHEN Yan-mei LI Xiao-ming CUI Ya-ru LU Xiao-tao |
| |
Affiliation: | School of Metallurgical Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, Shannxi, China |
| |
Abstract: | The mass loss rate of CaF2-CaO-Al2O3-SiO2-MgO slag system originated from ANF-6 was studied with CaF2, CaO, Al2O3, SiO2 or MgO content as variables. The method of quadratic regression orthogonal design was used for the design and analysis of the experiment. The experimental results indicated that mass loss rate of slag can be increased by 6% with CaF2 changing from 50% to 65%. Mass loss increases with SiO2, Al2O3 and MgO adding and decreases with CaO content increasing. Because of the reaction between oxide and fluoride in the slag pool, apparent mass loss of CaF2-Al2O3-CaO-SiO2-MgO slag system appears at melting point. This will cause obvious composition change of electroslag. In addition, the segregation occurs in the slag skin forming process. This is another reason causing the composition change of electroslag. |
| |
Keywords: | electroslag DSC-TG analysis quadratic regression orthogonal design composition change |
本文献已被 维普 万方数据 等数据库收录! |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《钢铁研究学报(英文版)》下载全文 |
|